FAKOLITH Aqua Isolier

PRODUCT SUMMARY: FAKOLITH AQUA ISOLIER is a high adhesion isolating primer with a white matte finish, to block and isolate visible migration and bleeding of pigmenting substances from the base coat to subsequent top coats.

Low Voc, low odor, high coverage, fast drying, easy to apply, with high adhesion to the base coat. Suitable as an adhesive bonding bridge and white insulating layer for surfaces with a wide variety of stain problems; dampness, lignin and wood derivatives, plasterboard marks, nicotine, fire mark damage, construction site markers, graffiti, etc.

Applicable on mineral bases of plaster, mortars, putties, laminated plaster panels, wood derivatives, plastics, aluminum, zink, and previous paints and coatings as long as they are well adhered to the base.

METHOD OF APPLICATION: For a good application of a product it is necessary to take into account the state and adequate preparation of the base.

Before its application, all those parts of badly adhered paints must be eliminated. In general the base must be clean, free of humidity and dust. If necessary, clean the base coat with the non-alkaline cleaners FK-12 (salts and microorganisms), FK-112 (greasy dirt), FK-9 (rust), rinse and let it dry. In certain very smooth and hard surfaces, a light sanding of the surface will favor its adequate adherence.

After homogenizing the FAKOLITH AQUA ISOLIER insulator, apply undiluted. Depending on the needs of each surface, apply 1 to 2 coats by brush, roller or:

- Airless Pressure 200-210 bar. Nozzle 0,010-15 inches
  In GRACO FFLP 410-411-412-413-413-414-415
- Airless air-assisted (air-mix) Pressure 140-160 bar.   
   Air 1-1,5 bar (same nozzles).
- High pressure equipment: 3-4 bar. Nozzle 1,8 mm
- Low pressure equipment: 0,48 bar. Nozzle 1,8 mm

Note: only if necessary for the application equipment add up to a maximum of 3% water, taking into account that it will be detrimental to the coverage.

CONSUMPTION - YIELD: It is variable, depending on the absorption, state of the surface and application method. Its average yield can range from 4-6 m²/l. when 2 coats are applied (50 microns equivalent layer) and 8-12 m²/l. when 1 coat is applied (25 microns equivalent layer).